The investigation of dye aging dynamics in writing inks using Raman spectroscopy

Опубликованно:Dyes and Pigments 131 (2016) 239-245

Kseniia O. Gorshkova, Ilya I. Tumkin, Liubov A. Myund, Andrey S. Tverjanovich, Andrey S. Mereshchenko, Maxim S. Panov, Vladimir A. Kochemirovsky

Abstract.The durability against light and aging dynamics of heteroatomic aromatic dyes and pigments containing nitrogen atoms used in writing inks was studied using Raman spectroscopy. The mechanisms of their thermal and photo-decomposition were proposed and the rates of these processes were determined. According to Raman spectroscopy, it was found that depending on the presence of one or another colorant, there are three main types (Type A, Type B and Type C) of blue dye inks used in ballpoint, gel and capillary pens which were studied in this work. Each type is characterized by a certain set of signals in Raman spectra. Time dependencies of Raman signal intensities for each type revealed the dynamics of the processes occurred with colorants included in the studied inks from the moment when they were printed on paper. Thus, the results obtained in this study can be used for the age estimation of the paper documents up to 15 years.

1. Introduction Despite the rapidly developing digital technologies, paper documents remain the primary source of information in many areas. A common way of document falsification is counterfeit the signatures, inscriptions and dates with ballpoint, gel and capillary pens. In some cases, in order to conceal the fraud the paper, documents are heated or irradiated by artificial and natural light sources. However, the identification of the date when a writing ink was printed on paper is one of the most difficult tasks in the field of criminology. Therefore, the study of the artificial and natural ink aging is an important criminalistic, judicial and social problem, which deserves particular attention and efforts. In order to create high-quality technique that meets all the requirements dictated by the specifics of the area under investigation, one should provide the detailed studies of all processes responsible for the property changes of ink components in time. The main components of writing inks are shown in Fig. 1. Here, the most interesting objects are dyes because they are least susceptible to temporal degradation among other components of writing inks. The proposed approach opens the possibility to identify documents up to 15 years due to the fact that the degradation of a dye is a long process.

When ink is applied on paper, a series of processes simultaneously occur: ink drying due to the solvent evaporation, solvent absorption on the surface of the paper and solvent diffusion inside the paper [1], ink fading due to degradation of colorants and ink solidification due to polymerization of resins [1e4]. The degradation of dyes is much slower than many other processes. This process may take several years under natural conditions due to photochemical reactions that occur during the absorption of visible or ultraviolet light. The absorption of a photon by an organic molecule leads to the formation of the electronically excited state, which results in the subsequent dye photodegradation [5e7]. Deactivation of the excited states of dyes is induced by the interaction with the environment because many radicals involved in the degradation reaction are formed from solvent or substrate upon light irradiation [8]. The photodegradation of a dye may occur due to several competing reactions:

  • a) N - demethylation. The methyl group of a dye is sequentially replaced by hydrogen when exposed to light [9] (Fig. 2).
  • b) Photooxidative cleavage of the central Cephenyl bond occurs probably via singlet oxygen resulting in benzophenone and phenol formation [9,10] (Fig. 3). It is known that the photolysis of triarylmethane dyes leads to formation of singlet oxygen not only in solution but even on paper [8,9,11]. As a result, in the absence of air under these conditions only leucobases are formed (colorless or weakly colored reduced forms of many organic dyes) [12].
  • c) Photoreduction of the excited dye cation to colorless leuco form. Here, the photoreduction of the excited dye cation is achieved by the addition of an electron to dye photoexcited states or by photochemical hydrogenation of a dye [9,13].
The investigation of dye aging dynamics in writing inks using Raman spectroscopy

It is necessary to note that dyes such as crystal violet and methyl violet are not stable and can decompose not only upon light irradiation but also in the dark due to oxidation by atmospheric oxygen. All these processes can occur at the same conditions and compete with each other. The writing inks usually consist of complex mixtures with various additives, solvents, resins. Moreover, materials of paper documents can also be very different in their structure and chemical composition. Therefore, it is quite important to study in detail the aging process of dyes taking into account all aforementioned factors [13].

2. Experimental

2.1. Materials and samples

All writing inks of various grades used in this work were commercially available and their types are presented in Supporting Information (SI, Table S1). We obtained the database of blue ink strokes of 1-cm length printed on paper at different time intervals (2000e2015 year). All samples were stored under the following conditions: temperature was kept at about 20 ± 5 C; the relative humidity was held at 70e95%; atmospheric pressure was 730e780 mm of Hg; without direct exposure to light, UV radiation and chemicals.

In order to study the influence of environmental factors on ink aging two groups of samples were prepared. In the first group, the ink strokes with a length of about 1 cmwere drawn on paper. In the second one, the strokes of solution of colorant in dimethyl formamide (DMFA) were drawn on paper by a glass rod. The choice of DMFA was based on its high dissolving capacity and suitability for spectroscopic studies in the near infrared region. Then all of these samples were subjected to heat and light exposure.

We used the following colorants in powder form: fat-soluble purple K, alcohol-soluble phthalocyanine blue, direct purple, basic purple K, acid purple, acid bright blue, pigment phthalocyanine blue, victoria blue, crystal violet, methyl violet, rhodamine G, basic blue lacquer K.

For spectrophotometric measurements the piece of a paper the sizes of 3  10 mm was stroked by the aforementioned inks. Also approximately the same paper area was stroked by the DMFA solutions of colorants using a glass rod.

For thin-layerchromatography (TLC), plates of Silufol (PTSH-AF-15  15) on the aluminum substrate were used. The chromatographic separationwas carried out in the next solvent system: ethyl acetate-isopropyl alcohol-water-acetic acid in a volume ratio of 30:15:10:1. The about 1 mg of each individual colorant was placed in microvial and dissolved in the 2 ml of DMFA for 2 h at the room temperature. The resulting dye solutions were transferred to the starting line on chromatographic plate using a microcapillary pipet. Before the chromatographic measurements, the TLC was stored at room temperature for 24 h. The zone detection was carried out visually in visible light.

The investigation of dye aging dynamics in writing inks using Raman spectroscopy

The investigation of dye aging dynamics in writing inks using Raman spectroscopy

2.2. Instrumentation

Raman spectra were obtained using a Senterra Raman spectrometer (Bruker Optics) equipped with three lasers with excitation wavelengths of 488, 532, 785 nm, a laser module confocal microscope (Olympus) and the fiber-optic sensor for spectra recording in an external sample compartment. A fully confocal system is able to operate at three different exciting wavelengths providing the highest possible spatial resolution at the same time. Raman spectra were recorded in the range of 440e1735 cm1. The baseline correction (two iterations) and smoothing (twenty five iterations) were performed for processing Raman spectra.

The electronic absorption spectra were recorded on a dual-beam scanning spectrophotometer Lambda 1050 with double monochromator using the module-integrating sphere of 150 mm (InGaAs). The measurements were carried out in the wavelength range of 450e850 nm. The spectral resolution was 2 nm.

Gas chromatographic analysis was performed using a Chromatec-Crystal 5000.2 chromatograph with dispenser for solid samples and a flame ionization detector. Analysis was performed using instrument parameters given in SI (Table S2). The strips of paper with studied ink strokes (each 1 cm long) were placed into the evaporator of the gas chromatograph using the dispenser for solid samples and kept there for 1 min.

To study thermal effects all samples were kept in the thermostat at 60 for the 7.25; 22.75; 35.25; 43.75 h and at 90 for 8.5; 23.5; 32.5; 56 h. To study the light effect all samples were irradiated with a xenon arc lamp (Oriel Instruments 67005 (output power 3.5 W)) for different times: 1, 3, 10, 30, 100 and 300 min. Alternatively, the studied samples were irradiated by the 355, 532 and 661-nm lasers. For normalization of obtained results we introduced the parameter E which was calculated using the next equation:

formula1

N e the output power measured using a power meter, W.; S e the area of the spot formed by the focused irradiation, m2; t e the irradiation time, s.

3. Results and discussion

Raman spectroscopy requires a selection of parameters in order to obtain spectra for samples of different kinds. In particular, one should take into account a number of criteria when working with inks deposited on paper. Thus, such criteria as laser power, exposure time and number of scans were optimized to ensure the best ratio signal-to-noise for all studied samples. Moreover, the absence of laser-induced degradation of the samples was also taken into consideration as another very important criterion. The lens of 50 times magnification used in the Raman experiments allowed to analyze the fully shaded portion of the ink stroke. As a result, a stroke size was sufficient enough for taking into account the inhomogeneity of ink distribution caused by the specificity of paper. In order to understand the influence of paper, the Raman spectra of paper substrates at each wavelength were recorded separately and then were subtracted from the Raman spectra of the ink containing samples.

3.1. Classification of writing inks

The Raman spectra of writing inks showed that colorants (dyes and pigments) have the most pronounced peaks, which were used for the classification of the samples. Thus, all the studied samples can be divided into three types of the Raman spectra recorded at 785 nm (Fig. 4) based on the presence of a characteristic group of peaks that correspond to one or another colorant (SI, Figs. S1eS3, Tables S3eS5).

However, writing inks attributed to the type B do not give distinct spectral characteristics at the wavelength of 785 nm due to strong contribution of luminescence. As a result, the useful Raman signal is too small to detect. Therefore, in order to conduct further analysis of samples of this type the Raman spectrawere recorded at 532 nm (SI, Fig. S2, Table S4). According to the interpretation of the obtained Raman spectra along with the results of TLC and spectrophotometric experiments, the following types of colorants were proposed:

  • 1 Type A e the alcohol-soluble phthalocyanine blue mixed with the triarylmethane group of dyes (such as basic violet, crystal violet, methyl violet, fat-soluble purple K, acid bright blue, victoria blue).
  • 2 Type B e the triarylmethane group of dyes.
  • 3 Type C e the phthalocyanine blue pigment.
The investigation of dye aging dynamics in writing inks using Raman spectroscopy

The spectrophotometric analysis of the samples (Table 1) confirmed the assumption that the Raman spectra obtained at different wavelengths are significantly different due to the influence of resonance (or preresonance) effects.

When the excitation frequency is close to the frequency of electronic-vibration transition an increase of scattering light occurs. This is especially important for the investigation of the multicomponent mixtures which have Raman spectra with hundreds of bands. When the wavelengths corresponding to the absorption maximum or near maximum in electronic spectra of colorants are applied, the optically active modes associated with chromophore group are substantially enhanced. In this regard, there is a possibility of selective isolation and identification of the substance in the studied matrix.

The Raman spectra recorded at 785 nm excitation show that the most intense bands correspond to the vibrations of the macrocyclic conjugated p-system which contains nitrogen atoms and carbon atoms of the central benzene ring in molecule of copper phthalocyanine. On the other hand, the most prominent bands of the Raman spectra obtained at 532 nm excitation correspond to the symmetric vibrations of the chromogen (Fuchsonimin) in triarylmethane dyes (Table 1) [14e22]. Furthermore, as it was proposed, the A-type writing inks contain a mixture of dyes and, therefore, if one apply the excitationwavelength near the absorption maximum of one or another dye it is possible to distinguish the peaks corresponding to each individual dye separately.

3.2. Natural aging

The temporal dependence of the ratios of the characteristic peak intensities for each type of writing ink is presented in Fig. 5.

Here, it should be pointed out that the peak intensities in the Raman spectra are also dependent on the concentration of the studied inks in the focal spot, which is impossible to control in our experiments. Therefore, we used not the absolute values of the peaks but the ratio of their intensities in order to eliminate the concentration influence [23]. For this purpose, the pairs of characteristic peaks were chosen as follows (Table 2): the first peak corresponds to the peripheral vibrations of bonds which are most susceptible to change during time and the second peak corresponds to the vibrations of the most stable bonds (usually stretching vibrations involving the carbon in the chromophore group).

In Fig. 5, each point on the graphs represents the average value of the ratios of the corresponding peaks obtained from five independent measurements of single sample. Herein, the X-axis is the time in months starting from the date when the writing ink was applied on a paper and up to the moment when the spectrum was taken. We believe that the complex form of the dependence is due to the change of dominant processes in a certain interval.

Type Colorant lmax (nm)
A alcohol-soluble phthalocyanine 610 - 620
670 - 680
triarylmethane group of dyes 530 - 580
B triarylmethane group of dyes 530 - 580
- ~ 650
С phthalocyanine blue pigment 670 - 680
- ~550
The investigation of dye aging dynamics in writing inks using Raman spectroscopy

3.3. Artificial aging

3.3.1. Aging induced by the irradiation with a xenon lamp

The xenon lamp was used to simulate ink aging process because its emission spectrum is close to the sunlight spectrum and, therefore, used to mimics daylight. The writing inks and pure colorants were deposited on paper 1 h before the irradiation (“fresh” ink strokes). Fig. 6 illustrates the dependencies of the ratios of the characteristic peaks on the irradiation time. These dependencies are demonstrated to be similar to those obtained in the case of the natural aging of the samples (Fig. 5). The presence of the first maximum in Fig. 6B could be caused by the influence of colorant matrix because solvents.

Resins can also contribute to the peak intensities in the Raman spectra. On the other hand, this maximumwas not observed for the pure colorant (Fig. 6A). Furthermore, Fig. 6A and B demonstrate similar behavior of these dependencies after 10 min of irradiation, probably meaning that the most likely further course of the curves is determined by only the degradation of colorants. Table 3 presents the correlation between the time of irradiation with a xenon lamp and the natural aging time obtained by comparison of the ratios of the peak intensities taken from Fig. 6 at the corresponding irradiation time with those shown in Fig. 5.

Triarylmethane dyes corresponding to B-type are less resistant to irradiation with respect to phthalocyanine dyes. Thus, Raman spectra exhibit no clearly distinguishable peaks after 30 min of irradiation; as a result, it is impossible to calculate the analytical ratios of the peak intensities.

The spectral range corresponding to the fastest dye degradation was determined. First, it was shown that the dependencies obtained after irradiation of the samples by the unfocused laser beam (Fig. 7) have the same shape as the initial part of those observed after irradiation with a xenon lamp (Fig. 6). The points on the curves corresponding to the ink aging experiments with a xenon lamp are a superposition of the ratios obtained after irradiation with lasers at certain wavelengths (Fig. 7).

Second, the shape of the dependencies for the samples acquired after laser irradiation at a wavelength of 355 nm has a more extreme character (more pronounced maxima) than those observed at wavelength of 532 and 661 nmdespite the fact that the latter are near the absorption maxima of colorants included in the writing ink composition. Therefore, it can be assumed that the dye degradation is mainly caused by the absorption of light in the UV range.

3.3.2. Aging caused by the temperature effect

The aging of dyes may be induced not only by the influence of light (photo-degradation) but also by temperature (thermodegradation). In this regard, in order to clarify the role of temperature in the ink aging process, the “fresh” ink strokes deposited on paper no later than 1 h prior the experiment were kept at different temperatures for a certain time. The overall results of this experiment are shown in Fig. 8.

The dependencies of the characteristic peaks on the heating time are linear with a small slope angle (Fig. 8A) for pure colorants, which may indicate a minor influence of temperature on the colorant degradation. Fig. 8B demonstrates that the curves characterizing the temperature effect for writing inks also exhibit linear behavior and the monotonic growth similarly to the initial part of the curves obtained in the natural aging experiments (Fig. 5). Thus, the aforementioned experiment indicates that the dye matrix is responsible for the increase of value of the peak ratios.

Type Colorant Raman peak (cm1) Vibration (n) Peak ratio
А alcohol-soluble phthalocyanine 1340 (C-C) ring 1340/1266
(C-N)
1266 SO2
В triarylmethane group of dyes 729 (C-N) 729/1587
1587 (C-C)ring
С phthalocyanine blue pigment 1340 (C-C) ring 1340/680
(C-N)
680 (C-C-H)
The investigation of dye aging dynamics in writing inks using Raman spectroscopy

Irradiation time, min The natural aging time, months
The investigation of dye aging dynamics in writing inks using Raman spectroscopy

3.4. Gas chromatography measurements

Gas chromatography was used to establish the time interval of the thermal degradation processes of the writing inks stored at natural conditions, in particular the solvent evaporation and decomposition of the ink components. Fig. 9 demonstrates the change of the chromatographic peak area corresponding to tetraethylene glycol, glycerol and 2-phenoxyethanol during the storage at the natural conditions.

It is shown here that the solvent evaporation occurs at a substantial speed only in the firstmonth after ink deposition (about 90% of solvent evaporates) then the evaporation process slows down dramatically. The presence of solvents in the ink stroke becomes insignificant after sixmonths of the natural aging. This time interval matches the initial part of the curves observed in Fig. 5. Analogically, the temperature influence on the artificial ink aging presented as a monotonic growth of the curve in Fig. 8B can also be explained by the solvent evaporation process. It is important observation because,for example, the presence of tetraethylene glycol determines the peak intensity at 1266 cm1, which in turn was used to plot corresponding dependencies in Fig. 8B. In this case, it is also necessary to take into account the presence of other solvents in the composition of inks. In addition, the growth of the initial part of the curve observed for the samples irradiated with a xenon lamp (Fig. 6B) and the unfocused laser beam (Fig. 7B) can be explained similarly.

The investigation of dye aging dynamics in writing inks using Raman spectroscopy

The investigation of dye aging dynamics in writing inks using Raman spectroscopy

The investigation of dye aging dynamics in writing inks using Raman spectroscopy

3.5. Dye aging model

Based on overall results discussed above, the dye degradation model is proposed. As an example let us consider the B-type colorant, which is based on the triarylmethane group of dyes. In order to plot the peak intensity ratios versus the exposition time (Fig. 10), Raman peaks at 729 cm1 corresponding to CeN vibrations and 1580 cm1 corresponding to the complex CeC variations of the chromogen (Fuchsonimin) were used.

These vibrations are sensitive to degradation in different extent due to specific nature of the Raman band. The graph shown in Fig. 10 can be split in three parts responsible for one or another dominant process:

  • The first part (Dt1) e the transformation of the dye matrix (volatile components evaporation, resin solidification).
  • The second part (Dt2) e N e demethylation (the methyl group of the dye is consistently replaced by hydrogen upon light irradiation).
  • The third part (Dt3) e the photooxidative cleavage of the central Cephenyl bond resulting in formation of benzophenone and phenol.

Fig. 10 illustrates the combination of the aforementioned processes dominating in certain time intervals.

4. Conclusion

The investigation of natural and artificial aging of writing inks printed on paper using Raman spectroscopy was performed. It was found out that the colorants determines the Raman spectra dynamics of the writing inks except for the initial period of ink aging process, which is accompanied by evaporation of volatile ink components. In the natural and artificial aging experiments, the key factor of long term degradation of the colorants and inks composed of them is light exposure. The impact of other components on the Raman spectral characteristics of the studied inks is manifested only within the initial period after ink deposition on paper (up to 6 months). The temperature within the range of 90e95 C has no significant effect on the Raman spectral properties of the colorants and corresponding dyes. Based on the obtained dependencies of the Raman peak intensities ratios versus the time exposure, the dye degradation model was proposed. It was suggested that there are several competing bond-breaking and bond-making reactions corresponding to the characteristic vibration frequencies of the dye molecule that simultaneously occur during ink aging process. Thus, the overall results of this work showed that Raman spectroscopy is an effective tool for studying the aging processes of the writing inks drawn on paper more than half a year after treatment. Moreover, these results can be implemented to develop the novel and promising method of criminology.

Acknowledgments

Authors acknowledge Saint-Petersburg State University for the financial support.Wewould like to thank E.R. Rossinskaya and Yu.G. Korukhov from Chamber of Judicial Experts (“Sudex”, Moscow) for their expertise and contribution to this project. The authors also express their gratitude to Centre for Optical and Laser Materials Research and Chemistry Educational Centre of Saint Petersburg State University.

Appendix A. Supplementary data

Supplementary data related to this article can be found at http://dx.doi.org/10.1016/j.dyepig.2016.04.009.

References

  • [1] Weyermann C, Almog J, Bugler J, Cantu AA. Minimum requirements for application of ink dating methods based on solvent analysis in casework. Forensic Sci Int 2011;210:52e62. http://dx.doi.org/10.1016/j.forsciint.2011.01.034.
  • [2] Weyermann C, Schiffer B, Margot P. A logical framework to ballpoint ink dating interpretation. Sci Justice 2008;48:118e25. http://dx.doi.org/10.1016/j.scijus.2007.10.009.
  • [3] Ezcurra M, Gongora JMG, Maguregui I, Alonso R. Analytical methods for dating modern writing instrument inks on paper. Forensic Sci Int 2010;197:1e20. http://dx.doi.org/10.1016/j.forsciint.2009.11.013.
  • [4] Lociciro S, Dujourdy L, Mazzella W, Margot P, Lock E. Dynamic of the ageing of ballpoint pen inks: quantification of phenoxyethanol by GC-MS. Sci Justice 2004;44:165e71. http://dx.doi.org/10.1016/S1355-0306(04)71709-8
  • [5] Stepanov BI. Introduction to chemistry and technology of organic dyes. Moscow: Chemistry; 1984.
  • [6] Coyle JD. Introduction to organic photochemistry. England: John Wiley & Sons; 1986.
  • [7] Dickert F, Becker HGO. 3., bearbeitete Auflage. In: B€otcher H, Dietz F, Rehorek D, Roewer G, Schiller K, Timpe H-J, editors. Einfuhrung in die Photochemie. Berlin: Deutscher Verlag der Wissenschaften; 1991. http://dx.doi.org/10.1002/bbpc.19930970423. ISBN 3-326-00604-7, 503 Seiten, Preis: DM 120,-. Berichte Der Bunsengesellschaft Fur Phys Chemie 1993;97: 643e643.
  • [8] Brezova V, Pigosova J, Havl? ? nova B, Dvoranova D, Durovic M. EPR study of photochemical transformations of triarylmethane dyes. Dye Pigment 2004;61: 177e98. http://dx.doi.org/10.1016/j.dyepig.2003.10.012.
  • [9] Caine MA, McCabe RW, Wang L, Brown RG, Hepworth JD. The influence of singlet oxygen in the fading of carbonless copy paper primary dyes on clays. Dye Pigment 2001;49:135e43. http://dx.doi.org/10.1016/S0143-7208(01) 00021-3.
  • [10] Kuramoto N, Kitao T. The contribution of singlet oxygen to the photofading of triphenylmethane and related dyes. Dye Pigment 1982;3:49e58. http://dx.doi.org/10.1016/0143-7208(82)80012-0.
  • [11] Caine MA, McCabe RW, Wang L, Brown RG, Hepworth JD. The inhibition of triphenylmethane primary dye fading in carbonless copying paper systems by singlet oxygen quenching bis(dithiocarbamato)nickel(II) complexes. Dye Pigment 2002;52:55e65. http://dx.doi.org/10.1016/S0143-7208(01)00076-6.
  • [12] Borodkin WF. Chemistry of dyes. Moscow: Chemistry; 1981.
  • [13] Weyermann C, Kirsch D, Vera CC, Spengler B. Evaluation of the photodegradation of crystal violet upon light exposure by mass spectrometric and spectroscopic methods. J Forensic Sci 2009;54:339e45. http://dx.doi.org/10.1111/j.1556-4029.2008.00975.x.
  • [14] Ziminov AV, Ramsh SM, Spiridonov IG, Yourre TA, Butkhuzi TG, Turiev AM. Synthesis and research of physical and chemical properties of phthalocyanines complexes with dand f-elements. Vestn Saint-Petersbg Univ; 2009. p. 95e109.
  • [15] Rosa A, Baerends EJ. Metal-macrocycle interaction in phthalocyanines: density functional calculations of ground and excited states. Inorg Chem 1994;33: 584e95. http://dx.doi.org/10.1021/ic00081a029.
  • [16] Mack J. Assignment of the optical spectra of metal phthalocyanines through spectral band deconvolution analysis and ZINDO calculations. Coord Chem Rev 2001;219e221:993e1032. http://dx.doi.org/10.1016/S0010-8545(01)00394-0.
  • [17] Panda DH. A concise guide on textile dyes, pigments and dye intermediates with textile printing technology. Niir Project Consultancy Services; 2013.
  • [18] Reichenb€acher M. Challenges in molecular structure determination. 2012. http://dx.doi.org/10.1007/978-3-642-24390-5.
  • [19] Garcia Rio L, Godoy A. Influence of CTACl cationic micelles on the spectral behavior of crystal violet. Chem Phys 2006;327:361e7. http://dx.doi.org/10.1016/j.chemphys.2006.05.008.
  • [20] Maruyama Y, Ishikawa M, Satozono H. Femtosecond isomerization of crystal violet in alcohols. J Am Chem Soc 1996;118:6257e63. http://dx.doi.org/10.1021/ja960024z.
  • [21] Oliveira CS, Branco KP, Baptista MS, Indig GL. Solvent and concentration effects on the visible spectra of tri-para-dialkylamino-substituted triarylmethane dyes in liquid solutions. Spectrochim Acta Part A Mol Biomol Spectrosc 2002;58:2971e82. http://dx.doi.org/10.1016/S1386-1425(02)00044-6.
  • [22] Ca~namares MV, Chenal C, Birke RL, Lombardi JR. DFT, SERS, and singlemolecule SERS of crystal violet. J Phys Chem C 2008;112:20295e300. http://dx.doi.org/10.1021/jp807807j.
  • [23] Petrov AA, Pushkarev EA. Correlation spectral analysis of substances. Saint Petersburg: Chemistry; 1993.

All Content Copyrait Межрегиональная Экономико Правовая Коллегия
Term & Condition | Privacy Policy